Composite Autoclave forming process
Composite High-pressure Vessel Molding Process
The composite high-pressure vessel molding process involves several steps. Firstly, a mold is prepared, which is typically made of steel or aluminum. The mold is carefully designed to have the desired shape and dimensions of the high-pressure vessel.
Next, the composite materials are prepared. This usually involves combining different types of fibers, such as carbon or glass fibers, with a matrix material, such as epoxy resin. The fibers are typically arranged in a specific pattern to provide the desired strength and stiffness to the final product.
Once the composite materials are prepared, they are placed into the mold. This can be done by hand or using automated machinery, depending on the size and complexity of the vessel. The materials are carefully layered and compacted to ensure proper distribution and consolidation.
After the materials are placed in the mold, the mold is closed and sealed. The vessel is then subjected to high pressure and temperature conditions. This is typically achieved using an autoclave or a pressurized oven. The high pressure and temperature help to cure the resin and bond the fibers together, resulting in a strong and durable composite structure.
After the curing process is complete, the mold is opened and the high-pressure vessel is removed. Any excess material is trimmed and the vessel is inspected for quality and dimensional accuracy. Additional finishing processes, such as sanding or painting, may be performed to achieve the desired surface finish.
In conclusion, the composite high-pressure vessel molding process involves preparing the mold, combining and compacting the composite materials, subjecting the vessel to high pressure and temperature, and finishing the final product. This process allows for the production of high-quality and high-performance composite high-pressure vessels.
Jiangsu Olymspan Equipment Eechnology Co.,Ltd
JIANGSU OLYMSPAN THERMAL ENERGY EQUIPMENT CO.,LTD is located in Changzhou city, not very far from Shanghai. We are a subcompany of WULIN group, which covers an area about 100,000 square meters, including 50,000 square meters building area. We have an experience team including about 200 skilled-workers, and more than 50 senior engineers. With over 20 years designing, manufacturing and trading experience in providing kinds of industrial equipments such as follows:
Carbon FIBER PRODUCTS
AEROSPACE AUTOCLAVE
COMPOSITE CURING AUTOCLAVE
AUTOCLAVE FOR CURING CARBONFIBER /PREPREGS
DEFENSE / MILITARY/ MARINES AUTOCLAVE
AUTOCLAVE CONTROL SYSTEM FOR COMPOSITE PRODUCT
AUTOCLAVE FOR AAC BRICK PRODOCTION LINE
AUTOCLAVE FOR CONCRETE PIPE PRODUCTION LINE
AUTOCLAVE FOR FIBER CEMENT BOARD PRODUCTION LINE
AUTOMATIVE LAMINATED GLASS PRODUTION LINE
AERATED AUTOCLAVE CONCRETE